Impact strength of simply supported beam without notch
-20°C
ISO 179
4.0 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179
10 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2
1450 Mpa
tensile strength
Yield
ISO 527-2
29.0 Mpa
Tensile strain
Break
ISO 527-2
50 %
Tensile modulus
ISO 527-2
1450 Mpa
Tensile stress
Yield
ISO 527-2
29 Mpa
Tensile strain
Break
ISO 527-2
50 %
Charpy Notched Impact Strength
-20℃
ISO 179
4.0 kJ/m²
Charpy Notched Impact Strength
23℃
ISO 179
10 kJ/m²
Rockwell hardness
ISO 2039-2
95
Impact strength of cantilever beam gap
ASTM D256/ISO 179
10 kg·cm/cm(J/M)ft·lb/in
Elongation at Break
ASTM D638/ISO 527
50 %
Tensile modulus
ASTM D638/ISO 527
1450 kg/cm²(MPa)[Lb/in²]
tensile strength
ASTM D638/ISO 527
29 kg/cm²(MPa)[Lb/in²]
Rockwell hardness
ASTM D785
95
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
105 °C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
105 °C
Hot deformation temperature
HDT
ASTM D648/ISO 75
105 ℃(℉)
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
melt mass-flow rate
230°C/2.16kg
ISO 1133
9.0 g/10min
melt mass-flow rate
230℃,2.16kg
ISO 1133
9.0 g/10min
density
ASTM D792/ISO 1183
0.91
melt mass-flow rate
ASTM D1238/ISO 1133
9.0 g/10min
hardness
شرایط آزمون
روش آزمون
نتیجه آزمون
Rockwell hardness
ISO 2039-2
95