thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
specific heat		ASTMC351	1260 J/kg/°C
Linear coefficient of thermal expansion	MD：-40到95°C	ASTME831	8.1E-05 cm/cm/°C
Heat Deflection Temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	149 °C
thermal conductivity		ASTMC177	0.21 W/m/K
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
RTI Str		UL 746	130 °C

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap		ASTM D1822	578 kJ/m²
Dart impact	23°C	ASTM D3029	149 J
Impact strength of cantilever beam gap	23°C	ASTM D4812	3200 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	370 J/m

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength	屈服,50.0mm跨距	ASTM D790	97.2 Mpa
flexural modulus	50.0mm跨距	ASTM D790	2330 Mpa
tensile strength	断裂	ASTM D638	77.9 Mpa
elongation	断裂	ASTM D638	78 %
tensile strength	屈服	ASTM D638	65.5 Mpa

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	300°C/6.1kg	ASTM D1238	9.0 g/10min
shrinkage rate	MD：3.20mm	内部方法	0.80-1.0 %
Water absorption rate	24hr	ASTM D570	0.19 %
Specific volume		ASTM D792	0.830 cm³/g
density		ASTM D792	1.19 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	2.0 g/10min

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
dielectric strength	3.20mm,inAir	ASTM D149	20 KV/mm
volume resistivity		ASTM D257	>2.5E+17 ohms·cm
dielectric constant	50Hz	ASTM D150	3.27
	dielectric constant	60Hz	ASTM D150	3.27
	dielectric constant	dielectric constant	1MHz	ASTM D150	3.10
Dissipation Factor	50Hz	ASTM D150	1.6E-03