Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	2270 Mpa
tensile strength	屈服	ASTM D638	57.0 Mpa
elongation	屈服	ASTM D638	5.0 %
elongation	elongation	断裂	ASTM D638	100 %
Flexural modulus	50.0 mm 跨距	ASTM D790	2340 Mpa
bending strength	屈服, 50.0 mm 跨距	ASTM D790	88.0 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dart impact	-30°C, Total Energy	ASTM D3763	54.0 J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	54.0 J

Electrical performance	روش آزمون	نتیجه آزمون
Compared to the Leakage Tracking Index (CTI)	UL 746	PLC 2
High arc combustion index (HAI)	UL 746	PLC 1
Hot wire ignition (HWI)	UL 746	PLC 3

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			100 to 110 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			30 to 80 %
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			250 to 290 °C
Temperature in the middle of the barrel			255 to 295 °C
Temperature at the front of the material cylinder			260 to 300 °C
Spray nozzle temperature			275 to 300 °C
Processing (melt) temperature			275 to 300 °C
Temperature			60 to 90 °C
Back pressure			0.300 to 0.700 Mpa
screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45 MPa, 未退火, 3.20 mm，HDT	ASTM D648	129 °C
Heat distortion temperature	Heat distortion temperature	1.8 MPa, 未退火, 3.20 mm，HDT	ASTM D648	112 °C
vicat		ISO 306/B50	130 °C
Linear coefficient of thermal expansion	-40 到 40°C，流动	ASTM E831	7.2E-5 cm/cm/°C
RTI Elec		UL 746	105 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	105 °C