برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون turbidity ASTM D1003 12 % gloss 45° ASTM D2457 45
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature Internal Method 122 °C Vicat softening temperature ASTM D1525 97.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 1.5 g/10min
film شرایط آزمون روش آزمون نتیجه آزمون Membrane strength TD ASTM D882 91.0 J/cm³ Membrane strength MD ASTM D882 82.7 J/cm³ Thin film puncture strength Internal Method 29.0 J/cm³ Thin film puncture strength Internal Method 62.3 N Thin film puncture strength Internal Method 5.65 J film thickness 25 µm Elmendorf tear strength TD ASTM D1922 600 g Elmendorf tear strength MD ASTM D1922 350 g Dart impact ASTM D1709A 650 g elongation TD:Break ASTM D882 500 % elongation MD:Break ASTM D882 400 % tensile strength TD:Break ASTM D882 37.9 Mpa tensile strength MD:Break ASTM D882 41.4 Mpa tensile strength TD:Yield ASTM D882 10.3 Mpa tensile strength MD:Yield ASTM D882 18.3 Mpa Secant modulus 2%Secant,TD ASTM D882 165 Mpa Secant modulus 1%Secant,TD ASTM D882 193 Mpa Secant modulus 2%Secant,MD ASTM D882 141 Mpa Secant modulus 1%Secant,MD ASTM D882 162 Mpa
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.