برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Suspended wall beam without notch impact strength 23°C ASTM D4812 1900 J/m Dart impact 23°C,TotalEnergy ASTM D3763 47.5 J
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.19mm UL 94 V-0 UL flame retardant rating 1.98mm UL 94 5VB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ASTM D638 3520 Mpa tensile strength Yield ASTM D638 63.4 Mpa tensile strength Break ASTM D638 49.0 Mpa elongation Yield ASTM D638 3.6 % elongation Break ASTM D638 80 % Bending modulus 50.0mmSpan ASTM D790 3140 Mpa bending strength Break,50.0mmSpan ASTM D790 106 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون RTI Imp UL 746 85.0 °C RTI UL 746 90.0 °C Hot deformation temperature 0.45MPa,Unannealed,3.20mm ASTM D648 92.2 °C Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 82.2 °C Vicat softening temperature ASTM D15256 102 °C Linear coefficient of thermal expansion MD:-40to40°C ASTME831 5.9E-05 cm/cm/°C Linear coefficient of thermal expansion TD:-40to40°C ASTME831 6.7E-05 cm/cm/°C RTI Elec UL 746 90.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 260°C/2.16kg ASTM D1238 16 g/10min Shrinkage rate MD:3.20mm Internal Method 0.30-0.50 % Shrinkage rate TD:3.20mm Internal Method 0.40-0.60 %