Impact strength of simply supported beam without notch
23°C
kJ/m²
45
Impact strength of simply supported beam without notch
-30°C
kJ/m²
40
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
Extreme Oxygen Index
%
37 --
Hot filament ignition temperature
3.00mm
°C
775 --
Hot filament ignition temperature
0.400mm
°C
700 --
Burning wire flammability index
3.00mm
°C
960 --
Flammability level
0.400mm
V-0 --
Burning wire flammability index
0.400mm
°C
960 --
Flammability level
1.50mm
V-0 --
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
bending strength
225 MPa
Bending modulus
MPa
9800 10800
Tensile strain
Break
%
2.1 1.9
tensile strength
Break
145 MPa
Tensile modulus
MPa
10700 11300
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Linear coefficient of thermal expansion
MD:-40to23°C
cm/cm/°C
1.8E-05 --
Linear coefficient of thermal expansion
MD
cm/cm/°C
1.8E-05 --
Melting temperature
°C
310 --
Hot deformation temperature
1.8MPa,Unannealed
°C
281 --
RTI Elec
3.00mm
°C
140 --
RTI Elec
1.50mm
°C
140 --
RTI Elec
0.750mm
°C
140 --
RTI Elec
0.400mm
°C
140 --
Linear coefficient of thermal expansion
MD:55to160°C
cm/cm/°C
1.2E-05 --
Linear coefficient of thermal expansion
TD
cm/cm/°C
6.2E-05 --
Linear coefficient of thermal expansion
TD:-40to23°C
cm/cm/°C
6E-05 --
Linear coefficient of thermal expansion
TD:55to160°C
cm/cm/°C
9.5E-05 --
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD
%
0.30 --
Shrinkage rate
TD
%
1.0 --
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Compared to the anti leakage trace index
V
--