برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 浸水24hrs后増重 ASTM D-570 0.3 % melt mass-flow rate ASTM D-1238 2 g/min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength 横夸比=16 ASTM D-790 1460(143) Kgf/cm Bending modulus ASTM D-790 34000 Kgf/cm tensile strength 初级Strain速率0.1cm/cm/min ASTM D-638 767(75) Kgf/cm Rockwell hardness ASTM D-758(M级) 99 Impact strength of cantilever beam gap 落锤(15.2*15.2*0.3cm)重1.4kg 半径0.64cm ASTM D-256 14(1.6) kg-cm(J) Impact strength of cantilever beam gap Lzod 研磨Notched ASTM D-256 1.5(14.7) kgf-cm/cm(J/m)
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature 50℃/hr,1kg ASTM D-1525 235 F Temperature range for use 与残余应力大小有关 85-105 Vicat softening temperature Unannealed ASTM D-1525 113 °C Hot deformation temperature HDT ASTM D-648 103 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-955 0.4-0.8 % density ASTM D-792 1.18 Flame retardant performance UL 94 HB CLASS Refractive index ASTM D-542 1.49 Transmittance rate ASTM D-1003 93 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.