برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256/ISO 179 5 kg·cm/cm(J/M)ft·lb/in Rockwell hardness ASTM D785 110 Bending modulus ASTM D412/ISO 527 14500 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 560 kg/cm²(MPa)[Lb/in²] tensile strength Yield ISO 527-1/-2 47 Mpa Tensile modulus Yield ISO 527-1/-2 4 % elongation Break ISO 527-1/-2 >200 % bending strength ISO 178 60 Mpa Bending modulus ISO 178 1500 Mpa Shore hardness ISO 868 77 D Rockwell hardness ISO 2039-2 105 R Charpy Notched Impact Strength 23℃ ISO 179/1eA 3C KJ/m Charpy Notched Impact Strength -40℃ ISO 179/1eA 3C KJ/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature 176-180 ℃(℉) Linear coefficient of thermal expansion ASTM D696/ISO 11359 10 mm/mm.℃ Hot deformation temperature 0.45Mpa ISO 75-2 95 °C Hot deformation temperature 1.8Mpa ISO 75-2 45 °C Linear coefficient of thermal expansion ISO 11359-2 1.3
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.02 kg·cm/cm(J/M)ft·lb/in Water absorption rate ASTM D570/ISO 62 0.25 % Melting temperature ISO 11357-3 179 °C Shrinkage rate ISO 294-4 0.9/0.9 % Water absorption rate ISO 62 0.6 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity ASTM D257/IEC 60093 10^15 Ω.cm Volume resistivity IEC 60093 10 Ω.cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.