برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256/ISO 179 39 kg·cm/cm(J/M)ft·lb/in tensile strength ASTM D638/ISO 527 67 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 94 Bending modulus ASTM D790/ISO 178 2940 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 98 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D638/ISO 527 30 % tensile strength ASTM D638 67 Mpa Elongation at Break ASTM D638 30 % bending strength ASTM D790 98 Mpa Bending modulus ASTM D790 2940 Mpa Impact strength of cantilever beam gap ASTM D256 39 J/m Rockwell hardness ASTM D785 94 M
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature HDT ASTM D648/ISO 75 170 ℃(℉) Hot deformation temperature HDT ASTM D648/ISO 75 136 ℃(℉) UL flame retardant rating UL 94 HB melt mass-flow rate ASTM D1238 9 g/10min Linear coefficient of thermal expansion TMA法 10 Hot deformation temperature 1.82MPa ASTM D648 136 °C Hot deformation temperature 0.45MPa ASTM D648 170 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.42 Shrinkage rate ASTM D955 1.8-2.2 % melt mass-flow rate ASTM D1238/ISO 1133 9 g/10min Water absorption rate ASTM D570/ISO 62 0.2 % Water absorption rate ASTM D570 0.2 % Shrinkage rate Flow 旭化成法 1.8-2.2 % Shrinkage rate Across Flow 旭化成法 1.8-2.2 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.