Instrumented dart impact energy peak at 23 ℃ (73 ℉)
/
ASTM D3763
7 J
Impact strength of cantilever beam gap
23℃ (73℉)80*10*4
ASTM D256
117 J/m
Impact strength of cantilever beam gap
23℃ (73℉)
ISO 180/1A
12 kJ/m²
Suspended wall beam without notch impact strength
23℃ (73℉)
ASTM D4812
1014 J/m
Suspended wall beam without notch impact strength
23℃ (73℉)80*10*4
ISO 180/1U
70 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Wear factor
Wear Fa
ASTM D 3702
6 E-10 in5·min/ft·lb·hr
Friction coefficient
Static C
ASTM D 3702
0.49 /
Friction coefficient
Dynamic
ASTM D 3702
0.46 /
Bending modulus
/
ISO 178
11230 Mpa
Bending modulus
/
ASTM D790
10820 Mpa
bending strength
/
ISO 178
280 Mpa
bending strength
/
ASTM D790
280 Mpa
Elongation at Break
/
ISO 527
2.5 %
Elongation at Break
/
ASTM D638
2.5 %
tensile strength
/,Break
ISO 527
196 Mpa
tensile strength
/,Break
ASTM D638
196 Mpa
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Water absorption rate
50% RH,
ASTM D 570
0.33 %
Shrinkage rate
xflow, 24,Across Flow
ISO 294
0.82 %
Shrinkage rate
xflow, 24,Across Flow
ASTM D 955
0.8 %
Shrinkage rate
flow, 24 h
ASTM D 955
0.2 %
Shrinkage rate
flow, 24 h
ISO 294
0.17 %