برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5mm UL 94 V-0 UL flame retardant rating 2.0mm UL 94 V-0 UL flame retardant rating 2.5mm UL 94 V-0 UL flame retardant rating 3.0mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus 3.20mm ASTM D638 2160 Mpa tensile strength Yield,3.20mm ASTM D638 39.2 Mpa elongation Yield,3.20mm ASTM D638 5.0 % elongation Break,3.20mm ASTM D638 >20 % Bending modulus 6.40mm ASTM D790 2350 Mpa bending strength 6.40mm ASTM D790 65.7 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed,6.40mm ASTM D648 89.0 °C Hot deformation temperature 1.8MPa,Unannealed,6.40mm ASTM D648 83.0 °C Vicat softening temperature ASTM D15256 90.0 °C RTI Elec UL 746 60.0 °C RTI Imp UL 746 60.0 °C RTI UL 746 60.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 220°C/10.0kg ASTM D1238 70 g/10min Shrinkage rate MD:3.20mm ASTM D955 0.40-0.70 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale ASTM D785 105