Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	53.9 Mpa
elongation	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	15 %
Flexural modulus	23°C, 3.20 mm, 注塑	ASTM D790	3330 Mpa
bending strength	23°C, 3.20 mm, 注塑	ASTM D790	98.1 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C, 3.20 mm, 注塑	ASTM D256	270 J/m

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			100 to 120 °C
drying time			3.0 to 5.0 hr
Suggested maximum moisture content			0.020 %
Minimum Moisture Content			0.020 %
Temperature at the rear of the barrel			280 to 295 °C
Temperature in the middle of the barrel			285 to 300 °C
Temperature at the front of the material cylinder			290 to 305 °C
Spray nozzle temperature			290 to 305 °C
Processing (melt) temperature			295 to 310 °C
Temperature			90 to 110 °C
Back pressure			0.981 to 3.92 Mpa
screw speed			40 to 70 rpm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8 MPa, 未退火, 6.40 mm, 注塑，HDT	ASTM D648	137 °C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	80.0 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.