برگه داده فنی مقایسهmachinability شرایط آزمون روش آزمون نتیجه آزمون Dry conditions 热风干燥 80℃---约3-4小时 Processing temperature 170 °C Processing temperature 190 °C Processing temperature 180 °C Processing temperature 180-210 °C Screw speed 80-120 rpm Mold temperature ≦40 °C
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ASTM D638/ISO 527 1600 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 1400 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 48 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D638/ISO 527 >100 % tensile strength 23℃ ASTM D638 34.3 Mpa Stretching length 23℃ ASTM D638 >300 % bending strength 23℃ ASTM D790 44.1 Mpa Bending modulus 23℃ ASTM D790 1.38 GPa Impact strength of cantilever beam gap 3.2mm ASTM D256 180 J/m Rockwell hardness ASTM D785 75 M
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Combustibility (rate) UL 94 HB Linear coefficient of thermal expansion ASTM D696/ISO 11359 1.2E-04 mm/mm.℃ UL flame retardant rating UL 94 HB Hot deformation temperature 455Kpa ASTM D648 147 °C Hot deformation temperature 820Kpa ASTM D648 94 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.35 Shrinkage rate ASTM D955 1.7 % melt mass-flow rate ASTM D1238 6.0 g/10min Shrinkage rate Flow 1.7 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D257 1×10 Volume resistivity ASTM D257 1×10
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.