برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ISO 527-2 3150 Mpa tensile strength Yield ISO 527-2 75.0 Mpa tensile strength -- ASTM D638 79.0 Mpa elongation Break ASTMD638 40 % Bending modulus -- ASTM D790 3040 Mpa Bending modulus -- ISO 178 2900 Mpa bending strength ASTM D790 108 Mpa Taber abraser ASTM D1044 13.0 mg
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion MD ASTMD696 1E-04 cm/cm/°C specific heat 1470 J/kg/°C thermal conductivity 0.23 W/m/K Hot deformation temperature 0.45MPa,Unannealed ASTM D648 172 °C Hot deformation temperature 0.45MPa,Unannealed ISO 75-2/B 167 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 136 °C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 103 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ISO 1133 1.7 g/10min Shrinkage rate MD Internal Method 1.8-2.2 % Water absorption rate 23°C,24hr,50%RH ASTM D570 0.20 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D257 1.0E+16-1.0E+17 ohms Volume resistivity 23°C ASTM D257 1.0E+15-1.0E+16 ohms·cm Dielectric strength ASTM D149 18 KV/mm Dielectric constant 23°C,1MHz ASTM D150 3.80 Dissipation factor 23°C,1MHz ASTM D150 7E-03 Arc resistance ASTM D495 250 sec
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ASTM D785 94 Rockwell hardness R-Scale ASTM D785 120
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.