Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
75 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
78 kJ/m²
Charpy Notched Impact Strength
-30°C
ISO 179/1eA
3.4 kJ/m²
Charpy Notched Impact Strength
23°C
ISO 179/1eA
3.7 kJ/m²
Bending modulus
23°C
ISO 178
3900 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
熔点
ISO 11359-2
265 °C
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/Af
75 °C
Hot deformation temperature
0.45MPaUnannealed
ISO 75-2/Bf
240 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Water absorption rate
(23°C,50RH)
ISO 62
2.3 %
Water absorption rate
(23°C,24hr)
ISO 62
0.80 %
Shrinkage rate
TD2.0mm
ISO 294-4
0.60 %
Shrinkage rate
MD2.0mm
ISO 294-4
0.90 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Dielectric strength
1.0mm
IEC 60243-1
17 KV/mm
Dissipation factor
耐电弧性
IEC 61621
120-179 S
Dissipation factor
相对漏电起痕指数
IEC 60112
600 V
Volume resistivity
IEC 60093
1E+10 Ω.cm
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL -94
V-0 0.71mm
Extreme Oxygen Index
ISO 4589-2
24 %
UL flame retardant rating
UL -94
V-0 3.00mm
UL flame retardant rating
UL -94
V-0 1.50mm