physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	320°C/2.16 kg	ASTM D1238	84 g/10 min
Shrinkage rate	流动 : 1.00 mm		0.030 %
Shrinkage rate	Shrinkage rate	横向流动 : 1.00 mm		0.40 %
Water absorption rate	平衡, 40°C, 95%RH		0.80 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating		UL 94	V-0
Bar Flow Length	320°C, 500.0 µm		7.10 CM
elongation at break		ASTM D638	0.30 %
Weld Strength		ASTM D638	35.0 Mpa

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength		ASTM D638	165 Mpa
elongation	断裂	ASTM D638	3.5 %
Flexural modulus		ASTM D790	15000 Mpa
bending strength		ASTM D790	225 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		ASTM D257	1.0E+16 ohms·cm
dielectric strength		ASTM D149	30 KV/mm
dielectric constant	10.0 GHz	ASTM D150	3.80
Dissipation Factor	10.0 GHz	ASTM D150	0.010
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 0

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8 MPa, 未退火，HDT	ASTM D648	285 °C
Glass Transition Temperature			125 °C
melting temperature			306 °C