برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap Notched1/4" ASTM D-256 18 kgcm/cm Elongation at Break ASTM D-638 18 % Rockwell hardness ASTM D-785 100 R-Scale tensile strength ASTM D-638 430 kg/cm2 Bending modulus ASTM D-790 24000 kg/cm2 Bending modulus ASTM D-790 710 kg/cm2
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Burning rate 1/8" UL -94 V-0 Hot deformation temperature Unannealed18.5kg/cm2,1/2" ASTM D-648 76 °C Burning rate 1/16" UL -94 V-0 Vicat softening temperature 1.000g ASTM D-1525 85 °C Burning rate 1/16" IEC 707 FV-0 mm/min
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D-792 1.20 melt mass-flow rate 220℃/10kg ASTM D-1238 60 g/10min Shrinkage rate ASTM D-955 0.004-0.007 mm/mm
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون High arc combustion index UL -746A PLC 0 High voltage arc tracing rate UL -746A PLC 2 Compared to the anti leakage trace index UL -746A PLCCode Hot wire ignition UL -746A Arc resistance ASTM D-495 PLC_7
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.