برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Reverse notch impact 3.20 mm ASTM D256 2100 J/m Suspended wall beam without notch impact strength 23°C ASTM D4812 2100 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5 mm UL 94 V-0 UL flame retardant rating 0.75 mm UL 94 V-2
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength Yield, 100 mm Span ASTM D790 144 Mpa Bending modulus 100 mm Span ASTM D790 3170 Mpa elongation Break ASTM D638 70 % tensile strength Yield ASTM D638 96.0 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون Spray nozzle temperature 350 to 370 °C Processing (melt) temperature 350 to 370 °C Mold temperature 135 to 165 °C Temperature at the front of the material cylinder 350 to 370 °C Temperature in the middle of the barrel 345 to 365 °C Temperature at the rear of the barrel 340 to 360 °C Suggested injection volume 40 to 60 % Suggested maximum moisture content 0.020 % drying time 4.0 to 6.0 hr drying temperature 135 °C Back pressure 0.300 to 0.700 Mpa Screw speed 40 to 70 rpm Exhaust hole depth 0.025 to 0.076 mm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون RTI UL 746 115 °C RTI Imp UL 746 115 °C RTI Elec UL 746 115 °C Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm ASTM D648 190 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 3.20 mm,Flow Internal Method 0.50 - 0.70 % melt mass-flow rate 337°C/6.6 kg ASTM D1238 24 g/10 min
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Hot wire ignition UL 746 PLC 0 High arc combustion index UL 746 PLC 4 Compared to the anti leakage trace index UL 746 PLC 4