thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat Deflection Temperature	1.80MPa未退火，HDT	ASTM D648	116 °C
Linear coefficient of thermal expansion	MD	ASTM D696	2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ASTM D696	6.7E-05 cm/cm/°C

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	23°C	ASTM D638	120 Mpa
Elongation at break	23°C	ASTM D638	2 %
Tensile modulus	23°C	ASTM D638	9050 Mpa
bending strength	23°C	ASTM D790	179 Mpa
flexural modulus	23°C	ASTM D790	8400 Mpa
Impact strength of cantilever beam gap	23°C	ASTM D256	150 J/m
Suspended wall beam without notch impact strength	23°C	ASTM D256	510 J/m

flame retardant performance	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating		UL -94	V-0 0.8mm

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
shrinkage rate	MD	ASTM D995	0.1 %
shrinkage rate	shrinkage rate	TD	ASTM D995	0.3 %
melt mass-flow rate	300℃/2.16Kg	ASTM D1238	25 g/10min

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.