برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C ISO 180/1A 9.0 kJ/m² Suspended wall beam without notch impact strength 23°C ISO 180/1U 50 kJ/m² Dart impact 23°C,EnergyatPeakLoad ASTM D3763 7.00 J Multi axis Instrumented Impact Energy ISO 6603-2 5.00 J
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength ASTM D790 195 Mpa Friction coefficient Dynamic ASTM D3702Modified 0.56 Friction coefficient Static ASTM D3702Modified 0.48 Wear factor Washer ASTM D3702Modified 11.0 10^-10in^5-min/ft-lb-hr Tensile modulus ASTM D638 10500 Mpa Tensile modulus ISO 527-2/1 9800 Mpa Bending modulus ASTM D790 7580 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 233 °C Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan ISO 75-2/Af 236 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:24hr ASTM D955 0.20 % Shrinkage rate TD:24hr ASTM D955 1.0 % Shrinkage rate TD:24hr ISO 294-4 0.97 % Shrinkage rate MD:24hr ISO 294-4 0.21 % Water absorption rate 24hr,50%RH ASTM D570 0.78 % Water absorption rate Equilibrium,23°C,50%RH ISO 62 1.2 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.