برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 230℃/3.8kg ASTM D-1238 8.1 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ASTM D-638 6620 Mpa tensile strength Yield ASTM D-638 82.0 Mpa tensile strength Break ASTM D-638 82.0 Mpa elongation at yield ASTM D-638 1.0 % Elongation at Break ASTM D-638 1.5 % Bending modulus 50.0mm Span ASTM D-790 6550 Mpa bending strength 50.0mm Span,Yield ASTM D-790 118 Mpa Impact strength of cantilever beam gap 23℃ ASTM D-256 37.4 J/m Suspended wall beam without notch impact strength 23℃ ASTM D-256 224 J/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed,3.20mm ASTM D-648 103 °C Hot deformation temperature 1.80MPa,Unannealed,3.20mm ASTM D-648 98.9 °C Vicat softening temperature ASTM D-1525 106 °C Linear coefficient of thermal expansion Flow,-40TO40℃ ASTM E-831 0.000036 cm/cm/℃ Linear coefficient of thermal expansion Transverse,-40TO40℃ ASTM E-831 0.000088 cm/cm/℃ Combustibility 1.50mm UL 94 HB
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate Flow,3.20mm ASTM D-955 0.20-0.40 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.