برگه داده فنی مقایسه

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness		ASTM D-758(M级)	97
transmittance		ASTM D-1003	92 %
density		ASTM D-792	1.19
refractive index		ASTM D-542	1.49
Shrinkage rate	(冷模/冷件),48hrs	ASTM D-935	0.2-0.6 %

Basic performance	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate		ASTM D-1238	3.5 g/10min
Water absorption rate	浸水24hrs后增重	ASTM D-570	0.3 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	Izod 研磨缺口	ASTM D256	1.2(12.3) kgf-cm/cm(J/m)
bending strength	横跨比=16	ASTM D-790	1050(103) Kgf/cm
Flexural modulus		ASTM D-790	32000 Kgf/cm
Impact strength of cantilever beam gap	落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm)	ASTM D256	14(1.4) kg-cm(J)
tensile strength	初级应变速度0.1cm/cm/min	ASTM D-638	720(70) Kgf/cm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Temperature range for use	与残余应力大小有关		85-102 °C
Heat distortion temperature	2℃/min,18.6kgf/cm，退火，HDT	ASTM D-648	102 °C
Glass Transition Temperature	Tg		108 °C
vicat	50℃/hr,1kg	ASTM D-1525，未退火	111 °C
vicat	vicat	50℃/hr,5kg	ASTM D-1525，未退火	104 °C