برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Suspended wall beam without notch impact strength 23°C ISO 180/1U 48 kJ/m² Impact strength of cantilever beam gap 23°C ISO 180/1A 10 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Break ASTM D638 151 Mpa Tensile modulus ISO 527-2/1 6800 Mpa Tensile modulus ASTM D638 7180 Mpa Wear factor Washer ASTM D3702Modified 140 10^-10in^5-min/ft-lb-hr Friction coefficient Static ASTM D3702Modified 0.48 Friction coefficient Dynamic ASTM D3702Modified 0.52 bending strength ISO 178 226 Mpa bending strength ASTM D790 241 Mpa Bending modulus ISO 178 6800 Mpa Bending modulus ASTM D790 7580 Mpa Tensile strain Break ISO 527-2 2.9to4.0 % elongation Break ASTM D638 3.4 % tensile strength Break ISO 527-2 155 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion TD:-40to40°C ISO 11359-2 6E-05 cm/cm/°C Linear coefficient of thermal expansion MD:-40to40°C ISO 11359-2 2.5E-05 cm/cm/°C Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan ISO 75-2/Af 205 °C Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 207 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24hr,50%RH ASTM D570 0.19 % Shrinkage rate MD:24hr ISO 294-4 0.30-0.50 % Shrinkage rate TD:24hr ISO 294-4 0.60-0.80 % Shrinkage rate TD:24hr ASTM D955 0.60-0.80 % Shrinkage rate MD:24hr ASTM D955 0.30-0.50 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.