برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 220℃/10kg ASTM D-1238 7 g/10min melt mass-flow rate 200℃/5kg ASTM D-1238 1 g/10min melt mass-flow rate 230℃/3.8kg ASTM D-1238 3 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 1/8" 23℃ ASTM D-256 19 kg-cm/cm Impact strength of cantilever beam gap 1/4" -30℃ ASTM D-256 8 kg-cm/cm Impact strength of cantilever beam gap 1/4" 23℃ ASTM D-256 18 kg-cm/cm Bending modulus 15mm/min ASTM D-790 25500 kg/cm bending strength 15mm/min ASTM D-790 750 kg/cm Elongation at Break 50mm/min ASTM D-638 20 % elongation at yield 50mm/min ASTM D-638 8 % Tensile modulus 1mm/min ASTM D-638 23000 % tensile strength Yield,50mm/min ASTM D-638 450 kg/cm Shore hardness R-scale ASTM D-785 110 Impact strength of cantilever beam gap 1/8" -30℃ ASTM D-256 8 kg-cm/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1/16" UL 94 HB calss UL flame retardant rating 1/8" UL 94 HB calss Hot deformation temperature 4.6kg/cm ASTM D-648 114 °C Hot deformation temperature 4.6kg/cm ASTM D-648 119 °C Hot deformation temperature 18.5kg/cm ASTM D-648 105 °C Hot deformation temperature 18.5kg/cm ASTM D-648 110 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-955 0.4-0.7 % density ASTM D-792 1.08 g/cc
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.