thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat Deflection Temperature	1.80MPa，HDT	ISO 75-1	105 °C
Heat Deflection Temperature	Heat Deflection Temperature	0.45Mpa，HDT	ISO 75-2	123 °C
vicat		ISO 306	121 °C
Linear coefficient of thermal expansion	平行方向	ISO 11359-2	0.8
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	垂直方向	ISO 11359-2	0.8
UL flame retardant rating		UL 94	HB

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-1	2450 Mpa
Tensile stress		ISO 527-1	60 Mpa
Tensile stress	Tensile stress	断裂	ISO 527-1	55 Mpa
elongation at yield		ISO 527-1	3 %
Elongation at break		ISO 527-1	110 %
flexural modulus		ISO 178	2500 Mpa
bending strength		ISO 178	90 Mpa
Impact strength of cantilever beam gap	没缺口	ISO 179	NB KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	带缺口	ISO 179	80 KJ/m

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
shrinkage rate	平行方向		0.5-0.7 %
shrinkage rate	shrinkage rate	垂直方向		0.5-0.7 %