برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون Extreme Oxygen Index ASTM D2863 29 % UL flame retardant rating 1.50mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength 3.20mm,Injection ASTM D790 97.9 Mpa Bending modulus 3.20mm,Injection ASTM D790 2830 Mpa elongation Break,3.20mm,Injection ASTM D638 50 % elongation Yield,3.20mm,Injection ASTM D638 4.0 % tensile strength Break,3.20mm,Injection ASTM D638 46.2 Mpa tensile strength Yield,3.20mm,Injection ASTM D638 62.1 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D15251 108 °C Hot deformation temperature 1.8MPa,Unannealed,Injection ASTM D648 82.2 °C Hot deformation temperature 0.45MPa,Unannealed,Injection ASTM D648 93.9 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD ASTM D955 0.40-0.60 % melt mass-flow rate 260°C/5.0kg ASTM D1238 75 g/10min melt mass-flow rate 230°C/3.8kg ASTM D1238 20 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.