برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D-1238 30 gr/10min Water absorption rate ASTM D-570 0.2 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D-256 59 J/m tensile strength ASTM D-638 61 Mpa bending strength ASTM D-790 90 Mpa Rockwell hardness ASTM D-785 115 R scale flexural coefficient ASTM D-790 2630 Mpa Rockwell hardness ASTM D-785 80 M Scale Elongation at Break ASTM D-638 50 % bending strength ASTM D790/ISO 178 90 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 2630 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 80 elongation ASTM D638/ISO 527 50 % tensile strength ASTM D638/ISO 527 61 kg/cm²(MPa)[Lb/in²] Impact strength of cantilever beam gap ASTM D256/ISO 179 59 kg·cm/cm(J/M)ft·lb/in
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa ASTM D-645 158 °C Hot deformation temperature 1.82MPa ASTM D-645 110 °C UL flame retardant rating UL 94 HB Linear coefficient of thermal expansion TMA 10 Hot deformation temperature HDT ASTM D648/ISO 75 110 ℃(℉) Hot deformation temperature HDT ASTM D648/ISO 75 158 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Wear factor ASTM D-1044 14 mg/1000次 Shrinkage rate 旭化成方法 1.6-2.0 % Water absorption rate ASTM D570/ISO 62 0.2 % melt mass-flow rate ASTM D1238/ISO 1133 30 g/10min Shrinkage rate ASTM D955 1.6-2.0 % density ASTM D792/ISO 1183 1.41
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.