برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C, Energy at Peak ASTM D3763 10.0 J Dart impact -- ISO 6603-2 2.00 J
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Break ASTM D638 139 Mpa tensile strength Break ISO 527-2 138 Mpa elongation Break ASTM D638 2.1 % Bending modulus ISO 178 9700 Mpa bending strength -- ASTM D790 236 Mpa bending strength -- ISO 178 211 Mpa Friction coefficient Dynamic ASTM D3702 0.58 Wear factor ASTM D3702 2.4E+6 10^-8 mm³/N·m
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 80 °C drying time 4.0 hr Suggested maximum moisture content 0.15 to 0.25 % Temperature at the rear of the barrel 265 to 275 °C Temperature in the middle of the barrel 280 to 295 °C Temperature at the front of the material cylinder 295 to 305 °C Processing (melt) temperature 280 to 305 °C Mold temperature 95 to 110 °C Back pressure 0.200 to 0.300 Mpa Screw speed 30 to 60 rpm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion Flow : -40 to 40°C ASTM E831 3.8E-5 cm/cm/°C Linear coefficient of thermal expansion Across Flow : -40°C ISO 11359-2 5.5E-5 cm/cm/°C
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.