physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
viscosity coefficient		ISO 307	102 CM
Water absorption rate	23℃,饱和	ISO 62	0.4 %
Water absorption rate	Water absorption rate	23℃,50%相对湿度	ISO 62	0.2 %
Shrinkage rate	纵向		0.2 %
Shrinkage rate	Shrinkage rate	横向		1.1 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-1/-2	10000 Mpa
tensile strength		ISO 527-1/-2	135 Mpa
elongation	断裂	ISO 527-1/-2	2.5 %
Tensile creep modulus		ISO 899-1	7500 Mpa
Impact strength of simply supported beam without notch	23℃	ISO 179/1eU	67 KJ/m
Charpy Notched Impact Strength	23℃	ISO 179/1eA	11 KJ/m
bending strength		ISO 178	200 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity	100Hz	IEC 60250	4
Volume resistivity	Volume resistivity	1MHz	IEC 60250	3.8
Dielectric dissipation factor	100Hz	亿厘60250	25 E-4
Dielectric dissipation factor	Dielectric dissipation factor	1MHz	IEC 60250	170 E-4
Volume resistivity		IEC 60093	1E+16 ohm.m
Compared to the Leakage Traceability Index (CTI)	A	IEC 60112	375
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI)	B	IEC 60112	125

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Melt volume flow rate		ISO 1133	11 CM
melting temperature		ISO 11357-1	223 °C
UL flame retardant rating		UL 94	HB
Heat distortion temperature	1.8Mpa，HDT	ISO 75-1/-2	215 °C
Heat distortion temperature	Heat distortion temperature	0.45Mpa，HDT	ISO 75-1/-2	220 °C
Linear coefficient of thermal expansion		ISO 11359-2	0.2-0.3 E-4/℃