برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB Burning rate FMVSS302 9.0 mm/min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength ISO 178 105 Mpa bending strength ASTM D790 105 Mpa Bending modulus ISO 178 5700 Mpa Bending modulus ASTM D790 5700 Mpa Tensile strain Break ISO 527-2 3.0 % elongation Break ASTM D638 3.0 % tensile strength Yield ISO 527-2 90.0 Mpa tensile strength Yield ASTM D638 90.0 Mpa Tensile modulus ISO 527-2 6000 Mpa Tensile modulus ASTM D638 6000 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature ISO 11357-3 165 °C Melting temperature ASTM D3417 165 °C Continuous use temperature --2 155 °C Continuous use temperature -- 100 °C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 145 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 145 °C Hot deformation temperature 0.45MPa,Unannealed ISO 75-2/B 153 °C Hot deformation temperature 0.45MPa,Unannealed ASTM D648 153 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 230°C/2.16kg ISO 1133 3.5 g/10min Shrinkage rate MD ASTM D955 0.10-0.40 % melt mass-flow rate 230°C/2.16kg ASTM D1238 3.5 g/10min Shrinkage rate ISO 2577 0.10-0.40 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.