برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C ASTM D256 50 J/m Bending modulus 23°C ASTM D790 12000 Mpa bending strength 23°C ASTM D790 140 Mpa Tensile modulus 泊松比 7.58 0.33 Tensile modulus 23°C ASTM D638 12500 Mpa Elongation at Break 23°C ASTM D638 1.1 % tensile strength 23°C ASTM D638 100 Mpa Friction coefficient 静态 ASTM D3702 0.35 Friction coefficient 动态 ASTM D3702 0.35
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion TD ASTM D696 1.8E-05 cm/cm/°C Linear coefficient of thermal expansion MD ASTM D696 1.8E-05 cm/cm/°C Hot deformation temperature 1.80MPaUnannealed ASTM D648 260 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate (23°C,24hr) ASTM D570 0.02 % Shrinkage rate TD ASTM D995 1.00 % Shrinkage rate MD ASTM D995 0.40 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dissipation factor 相对漏电起痕指数 ASTM D3638 190 V Dielectric strength 1.60mm ASTM D149 16 KV/mm Volume resistivity ASTM D257 1E+16 Ω.cm Dissipation factor 耐电弧性 ASTM D495 160 S Dissipation factor 23°C ASTM D150 6E-03 1MHz Dielectric constant 23°C ASTM D150 5.0 1MHz
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness ASTM D785 120 R Rockwell hardness ASTM D785 100 M(Scale)
flame retardant performance شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL -94 V-0 0.800mm