Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
170 kJ/m²
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
70 kJ/m²
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPaUnannealed
ISO 75-2/Bf
140 °C
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/Af
57.0 °C
Vicat softening temperature
Melting Temperature
ISO 11357-3
223 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
1.3E-04 cm/cm/°C
Linear coefficient of thermal expansion
导热系数
DIN 52612
0.27 W/m/K
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ISO 1183
1.31 g/cm³
Shrinkage rate
MD2.0mm
ISO 294-4
1.5 %
Shrinkage rate
TD2.0mm
ISO 294-4
1.5 %
Water absorption rate
(23°C,24hr)
ISO 62
0.40 %
Water absorption rate
(23°C,50RH)
ISO 62
0.20 %
melt mass-flow rate
250℃/2.16Kg
ISO 1133
55.0 cm3/10min
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
1E+18 Ω.cm
Dielectric constant
23°C
IEC 60250
3.30 100HZ
Dielectric constant
23°C
IEC 60250
3.30 1MHz
Dissipation factor
23°C
IEC 60250
1.3E-03 100HZ
Dissipation factor
23°C
IEC 60250
0.020 1MHz
Dissipation factor
相对漏电起痕指数
IEC 60112
500 V
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL -94
HB 0.800mm
UL flame retardant rating
UL -94
HB 1.60mm