برگه داده فنی مقایسهmachinability شرایط آزمون روش آزمون نتیجه آزمون Dry conditions 98℃ 2-3小时 Processing temperature 155-175 °C Processing temperature 185-195 °C Processing temperature 185-190 °C Processing temperature 190-200 °C Mold temperature 20-30 °C
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون elongation Break ISO 37 470 % tear strength ISP 34-1:2004(E) 170 kN/m Resilience ISO 4662 35 % Friction coefficient DIN 53516 50 mg Tensile stress 100%伸长率 ISO 37:2005(E) 12 Mpa Tensile stress 300%伸长率 ISO 37 22 Mpa tensile strength ISO 37 46 Mpa Tensile modulus 100% ASTM D412/ISO 527 12 Mpa/Psi Tensile modulus 300% ASTM D412/ISO 527 22 Mpa/Psi tensile strength ASTM D412/ISO 527 46 Mpa/Psi tear strength ASTM D624/ISO 34 170 n/mm² Shore hardness ASTM D2240/ISO 868 95+-2 Shore A Resilience ASTM D2630/ISO 4662 35 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ISO 306 120 °C Vicat softening temperature ASTM D1525/ISO R306 120 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ISO 868:2006(E) 95±2/49 density ASTM D792/ISO 2781/JIS K7311 1.2
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.