برگه داده فنی مقایسهOther performance شرایط آزمون روش آزمون نتیجه آزمون bending strength ASTM D-1052 >1×105
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24hr ASTM D-570 0.7 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ASTM D790/ISO 178 207 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 55 elongation ASTM D412/ISO 527 10.3 ℃(℉) tensile strength ASTM D412/ISO 527 40 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D412/ISO 527 6.9 % Elongation at Break ASTM D412/ISO 527 500 % Elongation at Break ASTM D-638 500 % Elongation at Break Break ASTM D-638 40 Mpa Initial tear strength ASTM D-1004 158 kN/m Shore hardness ASTM D-2240 55 Impact strength of cantilever beam gap 23℃ ASTM D-256 不破裂 J/m tensile strength 10%伸长 ASTM D-638 10.3 Mpa tensile strength 5%伸长 ASTM D-638 6.9 Mpa Rubbing modulus 23℃ ASTM D-790 207 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature 203 ℃(℉) Vicat softening temperature ASTM D1525/ISO R306 180 ℃(℉) Melting temperature ASTM D-3418 203 °C Hot deformation temperature @0.18Mpa ASTM D-648 49 °C Vicat softening temperature ASTM D-1525 180 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Taber abraser H 18轮 ASTM D-1044 112 mg/1000rev melt mass-flow rate ASTM D-1238 8.5 g/10min Hot deformation temperature @0.5Mpa ASTM D-648 90 °C Taber abraser CS-17轮 ASTM D-1044 - mg/1000rev density ASTM D955 1.2 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.