Impact strength of simply supported beam without notch
23℃ (73℉)
ISO 179/1eU
NB kJ/m²
Charpy Notched Impact Strength
23℃ (73℉)
ISO 179/1eA
7 kJ/m²
Suspended wall beam without notch impact strength
23℃ (73℉)
ISO 180/1U
NB kJ/m²
Suspended wall beam without notch impact strength
23℃ (73℉)
ISO 180/1A
7.5 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Bending modulus
23°C
ISO 178
4100 Mpa
bending strength
23°C
ISO 178
165 Mpa
Elongation at Break
50mm/m
ISO 527-2/1A
45 %
tensile strength
50mm/m,Yield
ISO 527-2/1A
100 Mpa
thermal properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Glass transition temperature (Tg)
-40°C to
ISO 11357-1/-2
143 °C
Melting temperature
-40°C to
ISO 11357-1/-3
343 °C
Linear coefficient of thermal expansion
Below Tg,Flow
ISO 11359-2
45 E-6 °C
Linear coefficient of thermal expansion
Above Tg,Flow
ISO 11359-2
120 E-6 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
/,Across Flow
ISO 294-4
1 .3 %
Shrinkage rate
/,Flow
ISO 294-4
1 %
melt mass-flow rate
ISO 1133
10 g/10min
Electrical Property
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
100000000000000 Ohm-m