برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 3.20mm ASTM D256 64 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 0.800mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون shear strength 2.00mm ASTM D732 55.0 Mpa bending strength 23°C ASTM D790 90.0 Mpa Bending modulus 23°C ASTM D790 2600 Mpa elongation Break,23°C ASTM D638 60 % tensile strength Yield,23°C ASTM D638 61.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed ASTM D648 110 °C Hot deformation temperature 0.45MPa,Unannealed ASTM D648 158 °C Linear coefficient of thermal expansion MD:20to80°C ASTM D696 1.3E-04 cm/cm/°C Hot deformation temperature Melting Temperature ASTM D648 165 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate Equilibrium,23°C,60%RH ASTM D570 0.22 % Shrinkage rate MD:3.00mm ASTM D955 2.0 % melt mass-flow rate ASTM D1238 9.0 g/10min density ASTM D792 1.41 g/cm³
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dissipation factor 1MHz ASTM D150 7E-03 Dielectric constant 1MHz ASTM D150 3.70 Dielectric strength ASTM D149 19 KV/mm Volume resistivity ASTM D257 1E+14 ohms·cm Surface resistivity ASTM D257 1E+16 ohms
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ASTM D785 80