thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat Deflection Temperature	0.45MPa,未退火,6.40mm，HDT	ASTM D648	92.0 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	86.0 °C
vicat		ASTM D15256	93.0 °C
RTI Elec		UL 746	60.0 °C
RTI Imp		UL 746	60.0 °C
RTI		UL 746	60.0 °C

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.8mm	UL 94	V-1
	UL flame retardant rating	2.0mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	3.20mm	ASTM D638	2060 Mpa
tensile strength	屈服,3.20mm	ASTM D638	44.1 Mpa
elongation	屈服,3.20mm	ASTM D638	5.0 %
elongation	elongation	断裂,3.20mm	ASTM D638	>20 %
flexural modulus	6.40mm	ASTM D790	2550 Mpa
bending strength	6.40mm	ASTM D790	73.5 Mpa

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	220°C/10.0kg	ASTM D1238	30 g/10min
shrinkage rate	MD：3.20mm	ASTM D955	0.40-0.70 %