Impact strength of simply supported beam without notch
23°C
ISO 179
24 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
0.8mm
UL 94
HB
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2
5800 Mpa
tensile strength
Break
ISO 527-2
110 Mpa
Tensile strain
Break
ISO 527-2
3.0 %
Bending modulus
ISO 178
5500 Mpa
bending strength
ISO 178
165 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
215 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
198 °C
Melting temperature
ISO 11357-3
224 °C
Linear coefficient of thermal expansion
MD:-30to50°C
ISO 11359-2
3E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD:-30to120°C
ISO 11359-2
3E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD:50to120°C
ISO 11359-2
3E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:-30to50°C
ISO 11359-2
9E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:-30to120°C
ISO 11359-2
1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion
TD:50to120°C
ISO 11359-2
1.4E-04 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
吸水率(Saturation,23°C)
0.080 %
Shrinkage rate
TD:2.00mm
1.3 %
Shrinkage rate
MD:2.00mm
0.50 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Dielectric strength
2.00mm
IEC 60243-1
21 KV/mm
Relative permittivity
1MHz
IEC 60250
3.20
Dissipation factor
1MHz
IEC 60250
0.020
Surface resistivity
IEC 60093
4E+16 ohms
Volume resistivity
IEC 60093
5E+16 ohms·cm
Dielectric strength
1.00mm
IEC 60243-1
24 KV/mm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.