برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,TotalEnergy ASTM D3763 16.9 J
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D638 74.5 Mpa tensile strength Break ASTM D638 74.5 Mpa elongation Break ASTM D638 4.2 % Bending modulus 100mmSpan ASTM D790 5310 Mpa bending strength Yield,100mmSpan ASTM D790 101 Mpa Friction coefficient Steel - Dynamic ASTM D1894 0.46 Friction coefficient Steel - Static6 ASTM D1894 0.30
thermal performance شرایط آزمون روش آزمون نتیجه آزمون RTI Elec UL 746 50.0 °C RTI Imp UL 746 50.0 °C RTI Str UL 746 50.0 °C Hot deformation temperature 0.45MPa,Unannealed,3.20mm ASTM D648 103 °C Hot deformation temperature 0.45MPa,Unannealed,6.40mm ASTM D648 105 °C Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 96.7 °C Hot deformation temperature 1.8MPa,Unannealed,6.40mm ASTM D648 99.4 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:3.20mm Internal Method 0.15-0.25 % Shrinkage rate TD:3.20mm Internal Method 0.25-0.45 % K (wear) coefficient Internal Method 73.0
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.