برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256/ISO 179 11 kg·cm/cm(J/M)ft·lb/in Elongation at Break ASTM D638/ISO 527 2.7 % tensile strength ASTM D638/ISO 527 40 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 58 kg/cm²(MPa)[Lb/in²] Charpy Notched Impact Strength ASTM D256/ISO 179 30 kg·cm/cm(J/M)ft·lb/in Charpy Notched Impact Strength ASTM D256/ISO 179 11 kg·cm/cm(J/M)ft·lb/in Impact strength of cantilever beam gap ASTM D256/ISO 179 31 kg·cm/cm(J/M)ft·lb/in Charpy Notched Impact Strength ASTM D256/ISO 179 160 kg·cm/cm(J/M)ft·lb/in
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature HDT ASTM D648/ISO 75 97 ℃(℉) Hot deformation temperature HDT ASTM D648/ISO 75 102 ℃(℉) Vicat softening temperature ASTM D1525/ISO R306 104 ℃(℉) Linear coefficient of thermal expansion ASTM D696/ISO 11359 0.8-1.1 mm/mm.℃
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.02 Shrinkage rate ASTM D955 0.4-0.7 % Water absorption rate ASTM D570/ISO 62 1.03 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.