برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Wear factor 0.060MPa,0.15m/sec7 JISK7218 4000 10^-8mm³/N·m Tensile modulus ISO 527-2 2250 Mpa tensile strength ISO 527-2 54.0 Mpa Nominal tensile fracture strain ISO 527-2 20 % Bending modulus ISO 178 2100 Mpa bending strength ISO 178 72.0 Mpa Friction coefficient Dynamic2 JISK7218 0.38 Friction coefficient Steel - Dynamic3 JISK7218 0.75 Wear factor 0.49MPa,0.30m/sec4 JISK7218 <1.0 10^-8mm³/N·m Wear factor 0.49MPa,0.30m/sec5 JISK7218 600 10^-8mm³/N·m Wear factor 0.060MPa,0.15m/sec6 JISK7218 1500 10^-8mm³/N·m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion MD:23to55°C Internal Method 1.2E-04 cm/cm/°C Linear coefficient of thermal expansion TD:23to55°C Internal Method 1.2E-04 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ISO 1133 19 g/10min Melt Volume Flow Rate (MVR) 190°C/2.16kg ISO 1133 18.0 cm3/10min Water absorption rate 23°C,24hr ISO 62 0.50 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity IEC 60093 5E+15 ohms Volume resistivity IEC 60093 7E+13 ohms·cm
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ISO 2039-2 80
Supplementary Information شرایط آزمون روش آزمون نتیجه آزمون ColourNumber CF2001