برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Charpy Notched Impact Strength 23°C ISO 179 16 kJ/m² Impact strength of cantilever beam gap -30°C,3.20mm ASTM D256 98 J/m Impact strength of cantilever beam gap -30°C,12.7mm ASTM D256 91 J/m Impact strength of cantilever beam gap 23°C,3.20mm ASTM D256 210 J/m Impact strength of cantilever beam gap 23°C,12.7mm ASTM D256 160 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength ASTM D638 44.0 Mpa tensile strength Yield,23°C ISO 527-2 54.0 Mpa elongation Break ASTM D638 15 % Tensile strain Break,23°C ISO 527-2 12 % Bending modulus ASTM D790 2500 Mpa Bending modulus 23°C ISO 178 2470 Mpa bending strength ASTM D790 77.0 Mpa bending strength 23°C ISO 178 82.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed,6.40mm ASTM D648 95.0 °C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 92.0 °C Vicat softening temperature 100 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.06 g/cm³ density 23°C ISO 1183 1.06 g/cm³ melt mass-flow rate 220°C/10.0kg ISO 1133 10 g/10min Shrinkage rate Internal Method 0.50-0.70 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Sale,23°C ASTM D785 115 Rockwell hardness R-Sale,23°C ISO 2039-2 115