برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C ISO 180/1A 12 kJ/m² Impact strength of cantilever beam gap 23°C,6.40mm ASTM D256 140 J/m Charpy Notched Impact Strength 23°C ISO 179/1eA 11 kJ/m²
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون elongation Break,3.20mm ASTM D638 20 % tensile strength Yield ISO 527-2/50 48.0 Mpa tensile strength Yield,3.20mm ASTM D638 47.1 Mpa Tensile modulus ISO 527-2/1 2200 Mpa bending strength ISO 178 75.0 Mpa bending strength 6.40mm ASTM D790 75.5 Mpa Bending modulus ISO 178 2400 Mpa Bending modulus 6.40mm ASTM D790 2300 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون RTI Imp UL 746 50.0 °C RTI Elec UL 746 50.0 °C Vicat softening temperature ISO 306/B50 102 °C Vicat softening temperature ASTM D15256 102 °C Hot deformation temperature 1.8MPa,Unannealed,4.00mm ISO 75-2/Ae 88.0 °C Hot deformation temperature 1.8MPa,Unannealed,6.40mm ASTM D648 94.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:3.20mm ISO 294-4 0.40-0.70 % Shrinkage rate MD:3.20mm ASTM D955 0.40-0.70 % melt mass-flow rate 220°C/10.0kg ISO 1133 6.0 g/10min melt mass-flow rate 220°C/10.0kg ASTM D1238 6.0 g/10min density ISO 1183 1.08 g/cm³ density ASTM D792 1.08 g/cm³
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness ISO 2039-2 104 Rockwell hardness R-Scale ASTM D785 104