برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 220℃/10.0kg ASTM D-1238 25 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap -30℃ ISO 179/1eA 8.00 KJ/m Impact strength of cantilever beam gap 23℃ 179/1eA 13.0 KJ/m Impact strength of cantilever beam gap -30℃ ASTM D-256 60.0 J/m Impact strength of cantilever beam gap 23℃ ASTM D-256 80.0 J/m Shore hardness ASTM D-2240 78 Tensile modulus ASTM D-638 2650 Mpa tensile strength Yield ASTM D-638 51.0 Mpa tensile strength Break ASTM D-638 34.0 Mpa elongation at yield ASTM D-638 2.8 % Elongation at Break ASTM D-638 10 % Bending modulus 50.0mm Span ASTM D-790 2600 Mpa bending strength 50.0mm Span,Yield ASTM D-790 77.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.80MPa,Unannealed,3.20mm ASTM D-648 83.0 °C Vicat softening temperature ASTM D-1525 89.0 °C Linear coefficient of thermal expansion Flow,-40TO40℃ ASTM E-831 0.000087 cm/cm/℃ Linear coefficient of thermal expansion Transverse,-40TO40℃ ASTM E-831 0.000085 cm/cm/℃ Combustibility 1.50mm UL 94 HB
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate Flow,3.20mm ASTM D-955 0.40-0.70 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.