برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Charpy Notched Impact Strength 23°C ISO 179 5.6 kJ/m² Impact strength of cantilever beam gap -40°C ASTM D256 45 J/m Impact strength of cantilever beam gap 23°C ASTM D256 64 J/m Impact strength of cantilever beam gap -40°C ISO 180 4.0 kJ/m² Impact strength of cantilever beam gap 23°C ISO 180 5.5 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus 23°C ISO 527-2 3700 Mpa tensile strength Break,23°C ASTM D638 85.0 Mpa tensile strength Break,23°C ISO 527-2 85.0 Mpa elongation Break,23°C ASTM D638 4.9 % Tensile strain Break,23°C ISO 527-2 4.9 % Bending modulus 23°C ISO 178 3270 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed ASTM D648 120 °C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 70.0 °C Melting temperature ASTM D3418 220 °C Melting temperature ISO 3146 220 °C Hot deformation temperature 0.45MPa,Unannealed ASTM D648 195 °C Hot deformation temperature 0.45MPa,Unannealed ISO 75-2/B 160 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.36 g/cm³ density ISO 1183 1.36 g/cm³ Shrinkage rate MD:3.18mm 0.90 % Water absorption rate Saturation ASTM D570 6.2 % Water absorption rate Saturation,23°C ISO 62 6.2 % Water absorption rate Equilibrium,50%RH ASTM D570 2.4 % Water absorption rate Equilibrium,23°C,50%RH ISO 62 2.4 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity 1.50mm ASTM D257 >1.0E+15 ohms·cm Volume resistivity IEC 60093 >1.0E+15 ohms·cm