برگه داده فنی مقایسهelastomer شرایط آزمون روش آزمون نتیجه آزمون tensile strength 50%Strain,3.20mm ASTM D412 4.10 Mpa tensile strength 100%Strain,3.20mm ASTM D412 5.50 Mpa tensile strength 300%Strain,3.20mm ASTM D412 11.7 Mpa tensile strength Break,3.20mm ASTM D412 34.5 Mpa elongation Break,3.20mm ASTM D412 600 % tear strength 3.20mm ASTM D624 105 kN/m Permanent compression deformation 25°C,22hr ASTM D395B 30 % Permanent compression deformation 70°C,22hr ASTM D395B 33 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Taber abraser 1000g,H-22Wheel ASTM D1044 20.0 mg
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Glass transition temperature DSC -40.0 °C Vicat softening temperature ASTM D15253 85.0 °C Linear coefficient of thermal expansion MD ASTM D696 1.7E-04 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 224°C/1.2kg ASTM D1238 40 g/10min Shrinkage rate MD ASTM D955 -0.20-0.50 % Shrinkage rate TD ASTM D955 0.60-0.80 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ShoreA ASTM D2240 82
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.