برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون turbidity ASTM D1003 1.3 % transmissivity Total ASTM D1003 91.0 % transmissivity Regular ASTM D1003 87.0 % gloss 60° ASTM D2457 143
impact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,EnergyatPeakLoad ASTM D3763 41.0 J Dart impact 0°C,EnergyatPeakLoad ASTM D3763 41.0 J Dart impact -40°C,EnergyatPeakLoad ASTM D3763 39.0 J Impact strength of cantilever beam gap 23°C ASTM D4218 NoBreak Impact strength of cantilever beam gap -40°C ASTM D4218 NoBreak Impact strength of cantilever beam gap 23°C ASTM D256 NoBreak Impact strength of cantilever beam gap -40°C ASTM D256 63 J/m
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Break,23°C ASTM D638 48.0 Mpa tensile strength Yield,23°C ASTM D638 47.0 Mpa Tensile modulus 23°C ASTM D638 1900 Mpa bending strength 23°C ASTM D790 65.0 Mpa Bending modulus 23°C ASTM D790 1900 Mpa elongation Yield,23°C ASTM D638 5.0 % elongation Break,23°C ASTM D638 300 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525 85.0 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 63.0 °C Hot deformation temperature 0.45MPa,Unannealed ASTM D648 73.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Color L ASTM D2244 95 Color b ASTM D2244 0.60 Color a ASTM D2244 -0.20 Shrinkage rate MD ASTM D955 0.30 % density ASTM D792 1.25 g/cm³
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Sale,23°C ASTM D785 105
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.