thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
RTI Imp		UL 746	85.0 °C
RTI		UL 746	90.0 °C
Heat Deflection Temperature	0.45MPa,未退火,3.20mm，HDT	ASTM D648	92.2 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	82.2 °C
vicat		ASTM D15256	102 °C
Linear coefficient of thermal expansion	MD:-40到40°C	ASTME831	5.9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40到40°C	ASTME831	6.7E-05 cm/cm/°C
RTI Elec		UL 746	90.0 °C

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.19mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.98mm	UL 94	5VB

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	3520 Mpa
tensile strength	屈服	ASTM D638	63.4 Mpa
tensile strength	tensile strength	断裂	ASTM D638	49.0 Mpa
elongation	屈服	ASTM D638	3.6 %
elongation	elongation	断裂	ASTM D638	80 %
flexural modulus	50.0mm跨距	ASTM D790	3140 Mpa
bending strength	断裂,50.0mm跨距	ASTM D790	106 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1900 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	47.5 J

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	260°C/2.16kg	ASTM D1238	16 g/10min
shrinkage rate	MD:3.20mm	内部方法	0.30-0.50 %
shrinkage rate	shrinkage rate	TD:3.20mm	内部方法	0.40-0.60 %