برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,TotalEnergy4 ASTM D3763 5.30 J Dart impact 23°C,TotalEnergy6 ASTM D3763 4.97 J Dart impact 23°C,TotalEnergy5 ASTM D3763 6.10 J
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ASTM D638 3560 Mpa tensile strength Yield ASTM D638 103 Mpa tensile strength Break4 ASTM D638 89.6 Mpa tensile strength Break ASTM D638 103 Mpa tensile strength Break ASTM D638 82.0 Mpa tensile strength Break ASTM D638 98.0 Mpa elongation Yield ASTM D638 4.0 % elongation Yield ASTM D638 97 % elongation Break4 ASTM D638 2.3 % elongation Break ASTM D638 4.0 % elongation Break ASTM D638 2.5 % Bending modulus 50.0mmSpan4 ASTM D790 5100 Mpa Bending modulus 50.0mmSpan ASTM D790 4640 Mpa Bending modulus 50.0mmSpan5 ASTM D790 4530 Mpa Bending modulus 50.0mmSpan6 ASTM D790 4820 Mpa bending strength Break,50.0mmSpan ASTM D790 150 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed,3.20mm ASTM D648 218 °C Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 193 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:3.20mm Internal Method 0.70-0.90 % Shrinkage rate TD:3.20mm Internal Method 1.0-1.2 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.