Impact strength of simply supported beam without notch
23°C
ISO 179
60 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL 94
HB
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
tensile strength
--
ASTM D638
52.0 Mpa
tensile strength
--
ISO 527-2/50
47.0 Mpa
elongation
Break
ASTM D638
22 %
elongation
Break
ISO 527-2/50
25 %
Bending modulus
--
ASTM D790
2200 Mpa
Bending modulus
--2
ISO 178
2300 Mpa
bending strength
--
ASTM D790
72.0 Mpa
bending strength
--2
ISO 178
65.0 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8MPa,Unannealed
ASTM D648
85.0 °C
Hot deformation temperature
1.8MPa,Unannealed5
ISO 75-2/A
78.0 °C
Vicat softening temperature
--
ASTM D15256
95.0 °C
Vicat softening temperature
--
ISO 306/B50
96.0 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
melt mass-flow rate
220°C/10.0kg
ASTM D1238
17 g/10min
melt mass-flow rate
220°C/10.0kg
ISO 1133
24 g/10min
Shrinkage rate
MD
ASTM D955
0.40-0.70 %
Shrinkage rate
--
ISO 294-4
0.40-0.70 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Surface resistivity
IEC 60093
>1.0E+15 ohms
Volume resistivity
IEC 60093
>1.0E+15 ohms·cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.